SABIC® HDPE M40053S

High Density Polyethylene Copolymer

Saudi Basic Industries Corporation (SABIC)

产品说明：

SABIC® HDPE M40053S is typically used for the high demanding dustbin market. It is an UV stabilized HDPE copolymer grade. It typically shows a good combination of processability, consistency and product properties, good stiffness/cold impact-balance, surface quality and weatherability properties.
Typical applications.
SABIC® HDPE M40053S is typically used for the manufacture of injection molded dustbins (waste containers on wheels and household containers), crates & boxes (pallet boxes, pallets, boxes applied at low temperatures) and pails & container applications (industrial, shipping).
This product is not intended for and must not be used in any pharmaceutical/medical applications.

物性信息：

基本信息
添加剂	紫外线稳定剂
特性	刚性，良好 高密度 共聚物 抗紫外线性能良好 可加工性，良好 耐低温冲击 耐气候影响性能良好 优良外观
用途	Pallets 废物容器 工业容器 家用货品 桶 装货箱 装运容器
加工方法	注射成型

物理性能	额定值	单位制	测试方法
密度	0.953	g/cm3	ISO 1183
熔流率（熔体流动速率）			ISO 1133
190°C/2.16 kg	4.0	g/10 min	ISO 1133
190°C/5.0 kg	11	g/10 min	ISO 1133
抗环境应力开裂 1(60°C, 3.00 mm, Rhodacal-DS10, 模压成型)	65.0	hr	内部方法

硬度	额定值	单位制	测试方法
肖氏硬度 (邵氏 D, 模压成型)	61		ISO 868

机械性能	额定值	单位制	测试方法
拉伸模量 (2.00 mm, 模压成型)	1050	MPa	ISO 527-2/1BA/50
拉伸应力			ISO 527-2/1BA/50
屈服, 2.00 mm, 模压成型	26.0	MPa	ISO 527-2/1BA/50
断裂, 2.00 mm, 模压成型	25.0	MPa	ISO 527-2/1BA/50
拉伸应变 (断裂, 2.00 mm, 模压成型)	> 200	%	ISO 527-2/1BA/50
弯曲模量 (2.00 mm, 模压成型)	1200	MPa	ISO 178
弯曲应力 (2.00 mm, 模压成型)	26.0	MPa	ISO 178

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度 (23°C, 模压成型)	4.0	kJ/m2	ISO 180/A

热性能	额定值	单位制	测试方法
热变形温度 (0.45 MPa, 未退火)	81.0	°C	ISO 75-2/B
维卡软化温度	124	°C	ISO 306/A
溶融温度（DSC）	132	°C	ISO 11357-3
Enthalpy Change	203	J/g	ISO 11357-3

注射	额定值	单位制
加工（熔体）温度	232 到 260	°C
模具温度	20.0 到 40.0	°C
注塑压力	93.0 到 103	MPa

备注
1 .	2 MPa